Thermal stability and spectroscopic properties of erbium-doped niobic-tungsten-tellurite glasses for laser and amplifier devices (Articolo in rivista)

Type

• Articolo in rivista (Classe)
• Prodotto della ricerca (Classe)

Label

• Thermal stability and spectroscopic properties of erbium-doped niobic-tungsten-tellurite glasses for laser and amplifier devices (Articolo in rivista) (literal)

Anno

• 2012-01-01T00:00:00+01:00 (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#doi

• 10.1016/j.jlumin.2011.12.057 (literal)

Alternative label

• A. Chiasera, M. Ferrari (2012)
  Thermal stability and spectroscopic properties of erbium-doped niobic-tungsten-tellurite glasses for laser and amplifier devices
  in Journal of luminescence
  (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#autori

• A. Chiasera, M. Ferrari (literal)

Pagina inizio

• 1265 (literal)

Pagina fine

• 1269 (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#numeroVolume

• 132 (literal)

Rivista

• Journal of luminescence (Rivista)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#affiliazioni

• N.G. Boetti, J. Lousteau, E. Mura, G.C. Scarpignato, D. Milanese [PhotonLab, Dipartimento di Scienza dei Materiali ed Ingegneria Chimica, Politecnico di Torino, Corso Duca degli Abruzzi 24, 10129 Torino, Italy] Silvio Abrate [PhotonLab, Istituto Superiore Mario Boella, Via P.C. Boggio, 61, 10138 Torino, Italy] Alessandro Chiasera, Maurizio Ferrari [CNR-IFN, Istituto di Fotonica e Nanotecnologie, CSMFO Lab. via alla Cascata 56/C, Povo, 38123 Trento, Italy] (literal)

Titolo

• Thermal stability and spectroscopic properties of erbium-doped niobic-tungsten-tellurite glasses for laser and amplifier devices (literal)

Abstract

• Er3+ doped niobic-tungsten-tellurite glasses doped with concentration of Er3+ ion up to 3 wt% were fabricated The effect of Er3+ doping concentration on thermal stability and optical properties was investigated in order to obtain the most suitable rare earth content for developing 1.5 um compact fiber amplifier pumped with a commercial telecom 980 nm laser diode. The maximum doping concentration allowed was found to be around 1.77x10^20 ions/cm3, for which a broad 1.5 um emission spectra of 65 nm FWHM and a lifetime of 3.4 ms for the 4I13/2 level was measured (literal)

Prodotto di

• Istituto di fotonica e nanotecnologie (IFN) (Istituto)
• Sviluppo e diagnostica ottica e spettroscopica di materiali e strutture per la fotonica (MD.P03.012.001) (Modulo)

Autore CNR

• ALESSANDRO CHIASERA (Persona)
• MAURIZIO FERRARI (Unità di personale interno)

Insieme di parole chiave

• Keywords of "Thermal stability and spectroscopic properties of erbium-doped niobic-tungsten-tellurite glasses for laser and amplifier devices" (Insieme di parole chiave)

Incoming links:

Prodotto

• Istituto di fotonica e nanotecnologie (IFN) (Istituto)
• Sviluppo e diagnostica ottica e spettroscopica di materiali e strutture per la fotonica (MD.P03.012.001) (Modulo)

Autore CNR di

• ALESSANDRO CHIASERA (Persona)
• MAURIZIO FERRARI (Unità di personale interno)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#rivistaDi

• Journal of luminescence (Rivista)

Insieme di parole chiave di

• Keywords of "Thermal stability and spectroscopic properties of erbium-doped niobic-tungsten-tellurite glasses for laser and amplifier devices" (Insieme di parole chiave)